| Composite: | Ferrite Magnet |
|---|---|
| Type: | Permanent |
| Application: | Industrial Magnet |
| Shape: | Powder |
| Coating: | as Customer Requirement |
| Composition: | Ferrite Magnet |
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier Type |
Material | Qualified standard of magnetic property | Rate of shrinkage (%) |
Average size | Water content of fine powder (%) |
Name used before | ||||||
| Br (mT) |
bHc (KA/m) |
iHc (KJ/m) |
(BH)max (KJ/m3) |
Testing direction | Spheric (mm) | Coarse powder (µm) | Fine powder (µm) |
|||||
| YXC-1 | Ferroxdure | ≥220 | ≥139 | ≥199 | ≥7.56 | // | 15±1 | 6~12 | 3~6 | 0.80~0.90 | ≤0.5 | Normal isomorphism barium |
| YXC-1R | Ferroxdure | ≥210 | ≥131 | ≥239 | ≥7.16 | ⊥ | 15±1 | 6~12 | 3~6 | 0.80~0.90 | ≤0.5 | Radial barium |
| YXC-1A | Ferroxdure | ≥230 | ≥143 | ≥239 | ≥8.36 | // | 15±1 | 6~12 | 3~6 | 0.80~0.90 | ≤0.5 | High performance isomorphism barium |
| YXC-3 | Strontium ferrite | ≥380 | ≥151 | ≥155 | ≥26.3 | // | 12±1 | 6~12 | 3~6 | 0.90~1.00 | ≤0.5 | Baric isomerism |
| YXC-4 | Strontium ferrite | ≥380 | ≥215 | ≥223 | ≥27.1 | // | 13±1 | 6~12 | 3~6 | 0.80~0.90 | ≤0.5 | Strontium isomerism |
| YXC-5 | Strontium ferrite | ≥400 | ≥223 | ≥231 | ≥30.2 | // | 13±1 | 6~12 | 3~6 | 0.70~0.80 | ≤0.5 | Y35 |
| YXC-5H | Strontium ferrite | ≥380 | ≥267 | ≥290 | ≥27.1 | // | 13±1 | 6~12 | 3~6 | 0.70~0.78 | ≤0.5 | Y34 |
| Grade | Max. Operational temperature |
| N35, N38, N40, N42, N45, N48, N50, N52 | 80° c |
| N33SH, N35SH, N38SH, N40SH, N42SH | 150° c |
| N28UH, N30UH, N33UH, N35UH, N38UH | Up to 180° c |
| N28EH, N30EH, N33EH, N35EH | Up to 200° c |
| N30AH, N33AH, N35AH | Up to 230° c |